Products : Bearings
High Anti-Corrosion Bearing Casstop
CASSTOP is a bearing realizing load-bearing performance with unique heat treatment technology for TBN-6H, a newly developed material showing corrosion resistance over conventional stainless steel SUS 440C or more. It demonstrates outstanding performance in acidic and alkaline environments of vessels and fishing tools exposed to salt water, medical equipment using antiseptic solution, etc.
Much higher corrosion resistance exceeding SUS440C is achieved by the optimum addition of four chemical element and fine adjustment on the content of other minimal elements.
Moreover, innovative heat treatment technology gives this material a hardness of HRC59.
Optimum internal design also enable this material to hold same of higher load resistance than SUS440C.
CASSTOP provides you higher stability and longer life to various machineries which are used in the environment such as salt water, rain water and alkali.
Application example
- machinery with salt water environment (Marine vessel, various equipment at port location, fishing tools)
- Machinery used in outside
- Environment with antiseptic solution.
- Fan motors for special environments
- Environment with pH 3 to pH 12 chemical solution (medical equipment, food processing equipment)
* Please contact about bearing size.
Load Capacity of CASSTOP
Video of CASSTOP usage example
High anti corrosion material bearing CASSTOPBearing material video
Main dimension
| Bearing Number | Main dimension (mm) | ||
|---|---|---|---|
| Inner diameter | Outer diameter | Width | |
| 692A-H-X1ZZ | 2 | 6 | 3 |
| SMR63A2-H-X1ZZ | 3 | 6 | 2.5 |
| 693A10-H-X1ZZ | 8 | 4 | |
| 623A3-H-X1ZZ | 10 | 4 | |
| SMR74A2-H-X1ZZ | 4 | 7 | 2.5 |
| SMR84A1-H-X1ZZ | 8 | 3 | |
| SMR104B-H-X1ZZ | 10 | 4 | |
| 694A1-H-X1ZZ | 11 | 4 | |
| 604A2-H-X1ZZ | 12 | 4 | |
| 624A5-H-X1ZZ | 13 | 5 | |
| SMR85A12-H-X1ZZ | 5 | 8 | 2.5 |
| SMR95A5-H-X1ZZ | 9 | 3 | |
| SMR105A2-H-X1ZZ | 10 | 4 | |
| SMR115B-H-X1ZZ | 11 | 4 | |
| 695A12-H-X1ZZ | 13 | 4 | |
| 625A6-H-X1ZZ1 | 16 | 5 | |
| SMR106A4-H-X1ZZ | 6 | 10 | 3 |
| SMR126A4-H-X1ZZ | 12 | 4 | |
| 686A6-H-X1ZZ | 13 | 5 | |
| 696A6-H-X1ZZ | 15 | 5 | |
| 606-H-X1ZZ | 17 | 6 | |
| 626B-H-X1ZZ1 | 19 | 6 | |
| SMR117A-H-X1ZZ | 7 | 11 | 3 |
| SMR137B-H-X1ZZ | 13 | 4 | |
| 687A5-H-X1ZZ | 14 | 5 | |
| 697A2-H-X1ZZ | 17 | 5 | |
| 607B-H-X1ZZ | 19 | 6 | |
| SMR128A5-H-X1ZZ | 8 | 12 | 3.5 |
| SMR148A2-H-X1ZZ | 14 | 4 | |
| 698-H-X1ZZ | 19 | 6 | |
| 689A3-H-X1ZZ | 9 | 17 | 5 |
High Anti-Corrosion Bearing CASSTOP Test Data
Anti-Corrosion test result of newly developed part "TBN-6H"
Performed at Nagano Prefecture Industrial Technology Center (8 hours spray 16 hours left × 10 cycles)
Saltwater spray test
Condition: sodium chloride (concentration = 50 ± 5 g / L)
ph. = 6.5 ~ 7.2 Temperature: 35 ° C ± 2 ° C for 10 days
 |
 |
 |
| ISC high anti-corrosion bearing CASSTOP | SUS440C | SUJ2 |
|---|
CASS test
Condition: Sodium chloride (concentration = 50 ± 5 g / L) - copper chloride (II) (concentration = 0.205 ± 0.015 g / L) solution
ph. = 3.1 - 3.3 Temperature: 50 ° C ± 2 ° C for 10 days
 |
 |
 |
| ISC high anti-corrosion bearing CASSTOP | SUS440C | SUJ2 |
|---|